Q

QUADRIPOLYMER: A polymer made from four distinct monomers.

QUALITY: See SECONDS and YARN QUALITY.

QUARTZ FIBER: Pure silica that has been melted and drawn into glass-like fibers. Used for

heat resistance and high dielectric strength.

QUENCH: 1. A box filled with water into which fabric is run after

singeing to prevent sparks or fires. 2. See CABINET. (Also see

QUENCHING.)

QUENCHING: The cooling of fiber filaments after extrusion by carefully

controlled airflow. (See CROSSFLOW QUENCH, INFLOW QUENCH,

and OUTFLOW QUENCH.)

QUENCH SPACER: The “quiet” zone below the spinneret in which there

is no quench airflow. Quench spacer distance is important in controlling

fiber orientation and birefringence.

QUETSCH: The nip rollers of a padding machine.

QUILL: A light, tapered tube of wood, metal, paper, or plastic on which the filling yarn is wound

for use in the shuttle during weaving.

QUILLING: The process of winding filling yarns onto filling bobbins, or quills, in preparation

for use in the shuttle for weaving.

QUILTING: 1. A fabric construction consisting of a layer of padding, frequently down or

fiberfill, sandwiched between two layers of material and held in place by stitching or sealing in a

regular pattern across the body of the composite. (Also see PINSONIC® THERMAL JOINING

MACHINE.) 2. The process of stitch bonding a batting or composite.

R

RACK: A warp-knitting measure consisting of 480 courses. Tricot fabric quality is judged by

the number of inches per rack.

RACKED STITCH: A knitting stitch that produces a herringbone effect with a ribbed back. It

is employed in sweaters for decorative purposes or to form the edge of garments. The racked

stitch is a variation of the half-cardigan stitch; it is created when one set of needles is displaced in

relation to the other set.

RACKING: A term referring to the side-to-side movement of the needles of the needle bed of a

knitting machine. Racking results in inclined stitches and reduced elasticity.

RADIANT PANEL TEST: See FLAMMABILITY TESTS.

RADIO-FREQUENCY DRYING: Use of radio-frequency electromagnetic radiation for drying

textiles. The application of RF to wet goods results in the selective heating of the water, which

has a partial polarity, because the molecule must do work to align in the RF field causing heat

generation within the water droplets. Non-polar materials, i.e., fabrics, are unaffected. RF drying

in very uniform and energy efficient when airflow patterns through the dryer are properly

designed and controlled.

RAILS: The metal bars on which the spindles of a downtwister are mounted.

RAISING: See NAPPING.

RAMIE: A bast fiber similar to flax obtained from the stalk of a plant grown in China, the U.S.,

and Japan.

RANDOM-SHEARED CARPET: A pile carpet with a textured face produced by shearing some

of the loops and leaving others intact.

RAPIER LOOMS: Looms in which either a double or single rapier (thin metallic shaft with a

yarn gripping device) carries the filament through the shed. In a single rapier machine, the yarn

is carried completely across the fabric by the rapier. In the double machine, the yarn is passed

from one rapier to the other in the middle of the shed. (Also see WEFT INSERTION.)

RASCHEL KNITTING: See KNITTING, 1.

RATINÉ: 1. A plain-weave, loosely constructed fabric having a rough, spongy texture which is

imparted by the use of nubby plied yarns. It is made from worsted, cotton, or other yarns. 2. A

variant of spiral yarns in which the outer yarn is fed more freely to form loops that kink back on

themselves and are held in place by a third binder yarn that is added in a second twisting

operation.

RAVEL: A type of comb or rail with projecting teeth for separating and guiding warp ends.

RAVELING: The process of undoing or separating the weave or knit of a fabric.

RAW FIBER: A textile fiber in its natural state, such as silk “in the gum” and cotton as it comes

from the bale.

RAYON FIBER: A manufactured fiber composed of regenerated cellulose, as well as

manufactured fibers composed of regenerated cellulose in which substituents have replaced not

more than 15% of the hydrogens of the

hydroxyl groups (FTC definition). Rayon

fibers include yarns and fibers made by the

viscose process, the cuprammonium process,

and the now obsolete nitrocellulose and

saponified acetate processes. Generally, in

the manufacture of rayon, cellulose derived

from wood pulp, cotton linters, or other

vegetable matter is dissolved into a viscose

spinning solution. The solution is extruded

into an acid-salt coagulating bath and drawn

into continuous filaments. Groups of these

filaments may be made in the form of yarns

or cut into staple.

CHARACTERISTICS: Rayon yarns are

made in a wide range of types in regard to

size, physical characteristics, strength,

elongation, luster, handle, suppleness, etc.

They may be white or solution dyed.

Strength is regulated by the process itself and

the structure of the yarn. (Also see

POLYNOSIC FIBER.)

Luster is reduced by including delustering materials, such as titanium dioxide pigments, in the

fiber when it is extruded. The suppleness of the yarn is controlled by the number of filaments in

the yarn, the denier or gauge of the individual filaments or fibers, and the fiber cross-section.

END USES: Rayon is used in draperies, bedspreads, upholstery, blanket, dish towels, curtains,

throw rugs, tire cord, industrial products, sport shirts, slacks, suitings, dress goods, and linings

and in blends with other fibers to enhance functional and aesthetic qualities, e.g., with polyester

in permanent-press fabrics.

REACTION SPINNING: See SPINNING, 2.

REAMING: Further plying of a two-ply yarn with a singles yarn. Reaming is not the same as

plying three singles yarns in one operation.

RECONSTITUTED FIBERS: Fibers made from recovered waste polymer or blends of virgin

polymer and recovered waste polymer.

RECOVERY: See ELASTIC RECOVERY.

RECREATIONAL SURFACES: Manufactured surfaces providing consistent properties,

durability, and special characteristics as needed for the specific application. Included are

artificial turf, pool decks, indoor-outdoor carpeting, tennis court surfaces, etc. Most types of

constructions (knit, woven, tufted, and nonwoven), and most polymer types find use in this

market. The polyolefins are particularly prominent in these applications.

REDUCTION CLEARING: The removal of unabsorbed disperse dye from the surface of

polyester at the end of the dyeing or printing process by treatment in a sodium hydroxide/sodium

hydrosulfite bath. A surface-active agent may be employed in the process.

REED: A comb-like device on a loom that separates the warp yarns and also beats each

succeeding filling thread against that already woven. The reed usually consists of a top and

bottom rib of wood into which metal strips or wires are set. The space between two adjacent

wires is called a dent (or split) and the warp is drawn through the dents. The fineness of the reed

is calculated by the number of dents per inch.

REED MARKS: A fabric defect consisting of warpwise light and heavy streaks in a woven

fabric, caused by bent, unevenly packed, or weak reed wires.

REEL: 1. A revolving frame on which yarn is wound to form hanks or skeins. 2. The frame on

which silk is wound from the cocoon. 3. A linen yarn measure of 72,000 yards. 4. The large

wheel in a horizontal warper onto which the warp sections are wound in the indirect system of

warping. 5. A spool of large capacity used to wind yarn or wire.

REELING: In silk fiber production, the process of unwinding the cocoon.

REFRACTIVE INDEX: See INDEX OF REFRACTION.

REFRACTORY FIBER: Oxide or non-oxide, amorphous or crystalline, manufactured fiber

generally used for applications at temperatures greater the 1063°C in both oxidizing and nonoxidizing

atmospheres, i.e., Al2O3, ZrO2, Al2O3.SiO2.

REGAIN STANDARD: See STANDARD MOISTURE REGAIN.

REGENERATED CELLULOSE: A material which begins as cellulose but at some stage in the

chemical processing takes the form of another chemical compound, then appears again in its

completed state as cellulose. Viscose and cuprammonium rayons are regenerated cellulose.

REINFORCEMENT FABRICS: See GEOTEXTILES.

RELATED SHADES: Colors of similar tone in the same or different depths.

RELATIVE HUMIDITY: The ratio of the actual vapor pressure of moisture in air to the

saturation vapor pressure at ambient temperature.

RELATIVE VISCOSITY: Ratio of the viscosity of the polymer in solution to that of the solvent

expressed as time of efflux of the solution divided by the time of efflux of the solvent at constant

temperature.

RELAXED YARN: A yarn treated to reduce tension and produce more uniform shrinkage or

torque. Relaxation produces more uniform dyeing characteristics in regular filament yarns of

nylon or polyester.

RELSET® PROCESS: A process of Richen, Inc., for continuous heat-setting of carpet or other

heavy yarns. Individual ends are continuously fed into a heat-setting chamber and withdrawn

into take-up cans or fed to winders.

REPACK ORDER: 1. An order requiring special packaging, as for export. 2. A small order for

a number of items requiring a breakdown of large cases.

REPEAT: The distance covered by a single unit of a pattern that is duplicated over and over,

measured along the length of a fabric.

REPELLENCY: The ability to resist wetting and staining by oils, water, soils, and other

materials.

RESERVE DYEING: See DYEING.

RESIDUAL SHRINKAGE: A term describing the amount of shrinkage remaining in a fabric

after finishing, expressed as a percentage of the dimensions before finishing.

RESILIENCY: Ability of a fiber or fabric to spring back when crushed or wrinkled.

RESIN: 1. A general term for solid or semi-solid natural organic substances, usually of vegetable

origin and amorphous and yellowish to brown, transparent or translucent, and soluble in alcohol

or ether but not in water. 2. Any of a large number of manufactured products made by

polymerization or other chemical processes and having the properties of natural resins.

RESIN-TREATED: Usually, a term descriptive of a textile material that has received an external

resin application for stiffening or an internal fiber treatment (especially of cellulosics) to give

wrinkle resistance or permanent press characteristics.

RESIST DYEING: See DYEING, Reserve Dyeing.

RESIST PRINTING: See PRINTING.

RESTRAINT SYSTEMS: An end use for textile fibers; restraint systems are devices such as air

bags, seat belts, and shoulder harnesses for passenger protection in automobile, trucks, airplanes,

etc.

RETARDER: A chemical that, when added to the dyebath, decreases the rate of dyeing but does

not affect the final exhaustion.

REVERSIBLE BONDED FABRIC: A bonded structure in which two face fabrics are bonded

together so that the two sides may be used interchangeable. There are limitations to the fabrics

that may be used because of increased fabric stiffness resulting from bonding.

REVOLVING SPINNING RING: A driven ring that rotates in the direction of the traveler on a

ring spinning frame. Since both the ring and the yarn package turn when this ring system is used,

productivity is increased.

RHEOLOGICAL PROPERTIES: The properties of viscous substances including polymers

that deal with deformation and flow. Includes viscosity and flow rate measurements.

RIBBING: A corded effect in a woven fabric that can be either lengthwise, crosswise, or

diagonal.

RIBBON: Narrow fabric made in several widths and a variety of weaves and used as a trimming.

RIB KNIT: A double-knit fabric in which the wales or vertical rows of

stitches intermesh alternately on the face and the back. In other words, odd

wales intermesh on one side of the cloth and even wales on the other. Ribknit

fabrics of this type have good elasticity, especially in the width.

RICKRACK: Flat braid in zigzag formation. It is produced by applying

different tensions to individual threads during manufacture.

RIDGY BEAM: A beam of yarn on which the ends are not evenly

distributed across the barrel, causing a profile of peaks (ridges) and

valleys. A ridgy beam can give poor removal characteristics.

RIDGY CLOTH: See BAGGY CLOTH.

RING: 1. A narrow band around hosiery appearing different from the rest of the hose. Principal

causes: variations in yarn size, dye, absorption, or luster. 2. The device that carries the traveler up

and down the package in ring spinning. (Also see RING SPINNING and REVOLVING RING

SPINNING.)

RINGER: 1. On a section beam, ringer is a term used for one or more filaments that have left the

parent end; as the beam revolves, the filaments continue to unwind, wrapping around the beam

(hence the word “ringer”). The severity of a ringer is dependent upon the number of filaments

contained therein at the time the filaments break. 2. In slashing, the term ringer is often used

when an end breaks on the slasher can, adheres to the can, and continues to wrap around it. This

condition should not be confused with ringers on the section beam.

RING-SPINNING: A system of spinning using a ring-and-traveler takeup

wherein the drafting of the roving and twisting and winding of the

yarn onto the bobbin proceed simultaneously and continuously. Ring

frames are suitable for spinning all counts up to 150’s, and they usually

give a stronger yarn and are more productive than mule spinning frames.

The latest innovation in ring spinning involves the use of a revolving ring

(Also see REVOLVING SPINNING RING) to increase productivity.

Ring spinning equipment is also widely used to take-up manufactured

filament yarns and insert producer-twist at extrusion.

RING SPINNING FRAME: See SPINNING FRAME.

RIPENING: Hydrolysis of cellulose acetate after acetylation to obtain the desired acetyl value.

This is generally accomplished by heat and agitation of the acid cellulose acetate solution under

controlled conditions of time, temperature, and acidity. Rapid ripening is accomplished by using

increased temperature for the reaction.

RIP OUT: See PICK-OUT MARK.

RIPPED SELVAGE: See CUT SELVAGE.

RISER: In textile fabric designing, a colored or darkened square on the design paper which

indicates that the warp end is over the filling pick at that point. The opposite of riser is sinker.

ROLLED ENDS: 1. On a section beam, rolled ends are adjacent ends that do not unwind parallel

to each other. Rolled ends can be caused by such factors as uneven tension, ridgy beams, and

static. 2. The ends can also roll behind the hook reed in slashing and can tangle with each other,

resulting in broken ends and ends doubling.

ROLLED SELVAGE: A curled selvage.

ROLLER CARD: Generally, any type of card in which rollers do the carding. Usually this

refers to a woolen card with a main cylinder and four to seven stripper rolls and worker rolls

working in pairs.

ROLLER PRINTING: See PRINTING.

ROLL GOODS: Fabric rolled up on a core after it has been produced. It is described in terms of

weight and width of the roll and length of the material on the roll.

ROLL LAPPING: A condition in which groups of fibers attach themselves to the drafting rolls

instead of following the normal path through the drafting system. These fibers cause the trailing

fibers to wind around the rolls and to bread the end down completely. Cleaning of the rolls is

required to remove the accumulated fiber.

ROPE: 1. A heavy, strong cord, made from either natural or

manufactured fibers or from wire, in a wide range of

diameters. Yarns are twisted together to form strands. These

strands are then twisted together in the opposite direction to

form the rope. The fact that the twist directions alternate at

different stages of rope assembly assures that the rope will be

twist-stable and will not kink during use. Also called cord.

2. Fabric in process without weft tension, thus having the

appearance of a thick rope.

ROPE MARK: A fabric defect consisting of long, irregular, longitudinal markings on dyed or

finished goods. A principal cause is abrasion while wet processing the fabric in rope form. Rope

marks are often related to overloading of the fabric during wet processing.

ROTARY SCREEN PRINTING: See PRINTING.

ROTOFLEX: A fatigue or endurance test developed by Goodyear for industrial yarns or cords.

ROTOR SPINNING: See OPEN-END SPINNING.

ROT RESISTANCE: The ability of textile materials to resist physical deterioration resulting

from the action of bacteria and other destructive agents such as sunlight or sea water.

ROUGH: A fabric condition in which the surface resembles sandpaper. Principal causes are the

shuttle rebounding in the box, jerky or loose shuttle tension, an incorrectly timed harness, and

wild twist in the filling.

ROUGH SELVAGE: See LOOPY SELVAGE.

ROVING: 1. In spun yarn production, an intermediate state

between sliver and yarn. Roving is a condensed sliver that

has been drafted, twisted, doubled, and redoubled. The

product of the first roving operation is sometimes called

slubbing. 2. The operation of producing roving (see 1). 3.

In the manufacture of composites, continuous strands of

parallel filaments.

ROVING FRAME: A general name for all of the machines

used to produce roving, different types of which are called

slubber, intermediate, fine, and jack. Roving frames draft

the stock by means of drafting rolls, twist it by means of a

flyer, and wind it onto a bobbin.

ROWS: In pile floor covering, the average number of tufts or loops per inch in the warpwise

direction.

RUB: See ABRASION MARK.

RUBBER FILAMENT: A filament extruded from natural or synthetic rubber and used as the

core of some elastic threads.

RUNNER: A break in the yarn of a knit fabric that causes the stitch to “run” along the needle

line (wale) in a vertical direction. (Also see END OUT.)

RUNNER LENGTH: In knitting, the number of inches of yarn from a warp to make one rack of

fabric.

RUN-OF-THE-MILL: See MILL RUN.

RUN-PROOF: A knitted construction in which the loops are locked to prevent runs.

RUN-RESISTANT: A type of knitting stitch that reduces runs.